Copper-chromium (CuCr) Contact for Vacuum Interrupter

  • Price:

    Negotiable

  • minimum:

  • Total supply:

  • Delivery term:

    The date of payment from buyers deliver within days

  • seat:

    Beijing

  • Validity to:

    Long-term effective

  • Last update:

    2017-09-11 09:54

  • Browse the number:

    800

Send an inquiries
+
Shaanxi Sirui Advanced Materials Co.,Ltd
Contactaixin:

somy344(Mr.)  

Email:

telephone:

phone:

Arrea:

Beijing

Address:

No.12 Zhangba 7th Road, High-tech Zone, Xi'an 710077-CHINA

Website:

http://www.sirui-material.com/ http://www.estonecarving.com/com/somy344/

+

Copper-chromium (CuCr) contact materials for  vacuum interrupter

Product Details:

1.The chemical composition and properties:

Material

Chemical Compositions (wt%)

Mechanical Properties

Cu

Cr

Gas Content

Hardness

HB (Mpa)

Density

(g/cm3)

Electrical Conductivity

(Ms/m)

O

N

CuCr50I

Balance

47.1-52.0

<0.050

<0.0040

80-120

≥7.90

≥16.0

CuCr10C

Balance

7.0-12.0

<0.050

<0.0030

70-100

≥8.60

≥40.0

CuCr25C

Balance

24.0-28.0

<0.080

<0.0050

70-105

≥8.30

≥28.0

CuCr30C

Balance

28.1-33.0

<0.080

<0.0050

75-110

≥8.20

≥26.0

CuCr40C

Balance

37.0-42.0

<0.080

<0.0050

80-120

≥8.00

≥20.0

CuCr40A

Balance

37.0-43.0

<0.060

<0.0030

85-125

≥8.00

≥20.0

CuCr50A

Balance

47.0-52.0

<0.060

<0.0030

85-140

≥7.90

≥18.0

CuCr25P

Balance

24.0-28.0

≤0.060

≤0.0050

70-105

≥8.10

≥28.0

CuCr30P

Balance

28.1-33.0

≤0.065

≤0.0050

75-110

≥7.90

≥26.0

Remark:C-vacuum casting;I-vacuum infiltration; A-vacuum arc-melting; P-Powder sintering

2.Some results of type tests as follow:


Material

Voltage

Contact   Size

Rated   current/Rated short-circuit current

CuCr50I

126kV

Ø100×5mm

2000A/40kA

40.5kV

Ø79×4.5mm

2000A/31.5kA

Ø76×5mm

1600A/25kA

12kV

Ø70×4mm

1600A/40kA

Ø82×5mm

3150A/50kA

Ø122×6mm

6300A/80kA

3.At the customer's request, contact parts  can be customered by special design.


4. Free samples can be offer.


5. Contact material in VI.